WHAT ARE THE DEFECTS OF BUILDING BRICKS ?

EFFLORESCENCE

This defect is caused because of alkalies present in bricks. When bricks come in contact with moisture, water is absorbed and the alkalis crystalise. On drying grey or white powder patches appear on the brick surface. This can be minimised by selecting proper clay materials for brick manufacturing, preventing moisture to come in contact with the masonry, by providing waterproof coping and by using water repellent materials in mortar and by providing damp proof course.

OVER BURNING OF BRICKS

Bricks should be burned at temperatures at which incipient, complete and viscous vitrification occur. However, if the bricks are overburnt, a soft molten mass is produced and the bricks loose their shape. Such bricks are not used for construction works.

UNDER BURNING OF BRICKS  

When bricks are not burnt to cause complete vitrification, the clay is not softened because of insufficient heat and the pores are not closed. This results in higher degree of water absorption and less compressive strength. Such bricks are not recommended for construction works.

BLOATING

This defect observed as spongy swollen mass over the surface of burned bricks is caused due to the presence of excess carbonaceous matter and sulphur in brick clay.

BLACK CORE

When brick-clay contains bituminous matter or carbon and they are not completely removed by oxidation, the brick results in black core mainly because of improper burning.

CHUFFS

The deformation of the shape of bricks caused by the rain water falling on hot bricks is known as chuffs.

LAMINATIONS

These are caused by the entrapped air in the voids of clay. Laminations produce thin lamina on the brick faces which weather out on exposure. Such bricks are weak in structure.

CHECKS OR CRACKS

This defect may be because of lumps of lime or excess of water. In case of the former, when bricks come in contact with water, the absorbed water reacts with lime nodules causing expansion and a consequent disintegration of bricks, whereas shrinkage and burning cracks result when excess of water is added during brick manufacturing.

BLOATING

This defect observed as spongy swollen mass over the surface of burned bricks is caused due to the presence of excess carbonaceous matter and sulphur in brick clay.

BLACK CORE

When brick-clay contains bituminous matter or carbon and they are not completely removed by oxidation, the brick results in black core mainly because of improper burning.

SPOTS 

Iron sulphide, if present in the brick clay, results in dark surface spots on the brick surfaces. Such bricks though not harmful are unsuitable for exposed masonry work.

BLISTERS

blisters are generally caused on the surface of sewer pipes and drain tiles due to air imprisoned during their moulding.

Related Post:-

DIMENSION TEST OF BUILDING BRICK(IS: 1077)
WATER ABSORPTION TEST OF BRICK (IS: 3495 (PART 2))

EFFLORESCENCE TEST OF BUILDING BRICK (IS: 3495 (PART 3)

WARPAGE TEST OF EARTHEN BRICK (IS-3495 (PART-4))

COMPRESSIVE STRENGTH TEST FOR BRICKS (IS-3495 (PART-1))HEAVY DUTY BURNT CLAY BUILDING BRICK ( IS: 2180 )

WHAT ARE THE VARIOUS TYPE OF BRICKS USED IN MASONRY ?

WHAT ARE THE ADMIXTURE TO MANUFACTURE OF BRICK ?

WHAT ARE THE METHOD USE TO MANUFACTURE EARTHEN BRICK ?

WHAT ARE THE INGREDIENTS OF GOOD BRICK EARTH ?